Step-shaped floating poly-si gate to improve gate coupling ratio for flash memory application

ABSTRACT

A stacked-gate flash memory cell is provided having step-shaped poly-gates with increased overlap area between them in order to increase the coupling ratio and hence the program speed of the cell. The floating gate is first formed with a step and the intergate dielectric is conformally shaped thereon followed by the forming of the control gate thereon. The increase in the overlap area can be achieved by forming gates with multiply connected surfaces of different shapes.

BACKGROUND OF THE INVENTION

1. (1) Field of the Invention

2. The present invention relates to the manufacturing of semiconductor memories, and in particular, is directed to a stacked-gate flash memory having a step-shaped floating polysilicon gate to improve its program speed, and also to a method of forming the same.

3. (2) Description of the Related Art

4. The higher the capacitive coupling between the floating gate and the control gate of a conventional stacked-gate memory cell, the higher is the program speed of the cell, as is well-known in the art. Capacitive coupling can be increased by increasing the capacitance, through an increase in the areas of the floating and control gate electrodes. On the contrary, however, because of the continued downscaling in the ultra large scale integration of semiconductor devices in general, the cell area, and hence the areas of the gate electrodes are necessarily being reduced. As a result, it has been difficult to maintain the same coupling levels, let alone increasing them. It is disclosed in the present invention a method of increasing the areas of the gate electrodes, without increasing the cell size, and hence that of the inter-dielectric layer between the gates. The coupling ratio, defined as the ratio of the area of the inter-dielectric layer to the area of the tunnel dielectric layer between the substrate and the floating gate is also increased, yielding a high program and erase speed for the stacked-gate memory cell, as described more fully below.

5. Although higher coupling ratios between the control gate and the floating gate can be supported by thinner inter-gate dielectric layers, or, inter-polygate oxides, data retention can cause concern due to leakages from thin layers. Also, word line voltages on control gates can be increased to increase programming and erase speeds. But, without the supporting larger area, which is provided in this invention, the situation exacerbates the well-known problem of junction break-down. It is shown later in the embodiments of this invention that larger areas can be achieved by forming gates with multiply connected surfaces of different shapes.

6. The importance of data retention capacity and the coupling ratio in a memory cell has been well recognized since the advent of the one-transistor cell memory cell with one capacitor. Over the years, many variations of this simple cell have been advanced for the purposes of shrinking the size of the cell and, at the same time, improving its performance. The variations consist of different methods of forming capacitors, with single, double or triple layers of polysilicon, and different materials for the word and bit lines.

7. Memory devices include electrically erasable and electrically programmable read-only memories (EEPROMs) of flash electrically erasable and electrically programmable read-only memories (flash EEPROMs). Generally, flash EEPROM cells having both functions of electrical programming and erasing may be classified into two categories, namely, a stacked-gate structure and a split-gate structure not discussed here. A conventional stacked-gate type cell is shown in FIG. 1 where, as is well known, tunnel oxide film (20), a floating gate (30), an interpoly insulating film (40) and a control gate (50) are sequentially stacked on a silicon substrate (10) between a drain region (13) and a source region (15) separated by channel region (17). Substrate (10) and channel region (17) are of a first conductivity type, and the first (13) and second (15) doped regions are of a second conductivity type that is opposite the first conductivity type.

8. The programming and erasing of the flash EEPROM shown in FIG. 1 is accomplished electrically and in-circuit by using Fowler-Nordheim (F-N) tunneling, as it is known in the art. Basically, a sufficiently high voltage is applied to control gate (50) and drain (13) while source (15) is grounded to create a flow of electrons in channel region (17) in substrate (10). Some of these electrons gain enough energy to transfer from the substrate to control gate (50) through thin gate oxide layer (20) by means of (F-N) tunneling. The tunneling is achieved by raising the voltage level on control gate (50) to a sufficiently high value of about 12 volts. As the electronic charge builds up on floating gate (30), the electric field is reduced, which reduces the electron flow. When, finally, the high voltage is removed, floating gate (30) remains charged to a value larger than the threshold voltage of a logic high that would turn it on. Thus, even when a logic high is applied to the control gate, the EEPROM remains off. Since tunneling process is reversible, floating gate (30) can be erased by grounding control gate (50) and raising the drain voltage, thereby causing the stored charge on the floating gate to flow back to the substrate.

9. The thicknesses of the various portions of the oxide layers on the stacked-gate flash memory cell of FIG. 1 play an important role in determining such parameters as current consumption, coupling ratio and the memory erase-write speed, especially in an environment where feature sizes in advanced integrated circuits are being scaled down at a rapid rate. In prior art, various methods have been developed to address these parameters. For example, EPROMs having a trench-like coupling capacitors have been disclosed to address the shrinking area of the gate electrodes, and hence the capacitive coupling ratio between the floating gate and control gates on a conventional prior art EPROM. In U.S. Pat. No. 5,801,415, Lee, et al., teach a method for making a such a trench-like coupling capacitor in a non-volatile memory cell from a single filed-effect transistor (FET) that incorporates a floating gate over the FET channel area. The floating gate also extends vertically upward on the sidewalls of the control gate, thereby increasing the capacitor area between the floating and control gates. Tseng of U.S. Pat. No. 5,677,216 also utilizes a trench with a floating gate so as to increase the surface area of the inter-poly in order to achieve a higher coupling ratio.

10. On the other hand, Tseng uses a different structure in U.S. Pat. No. 5,451,537 in forming a stack capacitor in a dynamic random access memory cell. Here, a bottom electrode is connected to an extends up from the source region of a MOS transistor, and has a top surface with a central cavity, and side surfaces extending down from the top surface in a step-like, or ladder, manner. These step-like sides are formed by a repeated tow-step process of removing a portion of the vertical walls of a photoresist mask and removing a portion of the top surface of a layer of polysilicon from which the bottom electrode is formed. Still another approach is taught by Liang, et al., in U.S. Pat. No. 5,714,412 for forming a multi-level, split-gate flash memory cell where a control gate spans a pair of floating gate electrodes. A method of programming a flash memory cell is taught by Bergemont of U.S. Pat. No. 5,464,999.

11. In the present invention, a differently shaped floating gate is disclosed for improving the coupling between the floating gate and control gate of a stacked-gate flash memory cell. The method employed is applicable for increasing the coupling ratio of the well-known Intel ETOX (EPROM with tunnel oxide) memory cell, as shown later in the embodiments of the present invention.

SUMMARY OF THE INVENTION

12. It is therefore, an object of this invention to provide a stacked-gate flash memory cell having an increased overlap area between the floating gate and the control gate with the associated increase in the gate coupling ratio for improved programming of the cell.

13. It is another object of this invention to provide a method of forming a stacked-gate flash memory cell having a step-shaped floating polysilicon gate in order to increase the gate coupling ratio of the cell.

14. These objects are accomplished by providing a semiconductor substrate; a floating Poly-Si gate with multiply connected surfaces of different shapes; an interpoly dielectric layer over said floating Poly-Si gate; and a Poly-Si control gate over said inter-poly dielectric layer.

15. These objects are further accomplished by providing a semiconductor substrate; forming a gate-oxide layer over said substrate; forming a first polysilicon layer over said gate-oxide layer; forming a pad-oxide over said first polysilicon layer; forming a nitride layer over said pad-oxide layer; patterning and forming an opening in said nitride layer to define a floating gate region in said substrate; forming a layer of spacer oxide over said nitride layer including said opening; etching said layer of spacer oxide to form oxide spacers in said opening and to expose said first polysilicon layer in said opening; performing a partial etch of said first polysilicon layer exposed in said opening to form a step-shaped surface on said first polysilicon layer; removing said oxide spacers from said opening; performing a re-oxidation of said first polysilicon layer in said opening to form a layer of poly-oxide over said step-shaped surface on said first polysilicon layer; using said layer of poly-oxide as a mask, etching said layers of nitride, pad-oxide and first polysilicon layer to form a floating Poly-Si gate with said step-shaped surface; forming a step-shaped inter-poly oxide layer over said substrate including said floating Poly-Si gate with said step-shaped surface; forming a second polysilicon layer over said step-shaped inter-poly oxide layer; removing said second polysilicon layer and underlying said inter-poly oxide layer from said substrate, excluding from regions over floating Poly-Si gate, thus forming a Poly-Si control gate having step-shaped surface corresponding to said floating Poly-Si gate with step-shaped surface; and performing ion implantation to form source and drain of said stacked-gate flash memory cell.

BRIEF DESCRIPTION OF THE DRAWINGS

16.FIG. 1 is a cross-sectional view of a conventional stacked-gate type memory cell of prior art.

17.FIG. 2a is a cross-sectional view of a semiconductor substrate showing the forming of a gate-oxide layer followed by the forming of a first polysilicon layer, according to this invention.

18.FIG. 2b is a cross-sectional view of a semiconductor substrate showing the forming of a nitride layer over the first polysilicon layer of FIG. 2a, according to this invention.

19.FIG. 2c is a cross-sectional view of a semiconductor substrate showing the patterning of the nitride layer of FIG. 2b, according to this invention.

20.FIG. 2d is a cross-sectional view of a semiconductor substrate showing the forming of a spacer oxide layer over the patterning of FIG. 2c, according to this invention.

21.FIG. 2e is a cross-sectional view of a semiconductor substrate showing the forming of oxide spacers, according to this invention.

22.FIG. 2f is a cross-sectional view of a semiconductor substrate showing the forming of a step in the first polysilicon layer of FIG. 2e, according to this invention.

23.FIG. 2g is a cross-sectional view of a semiconductor substrate showing the oxidation of the first polysilicon layer, according to this invention.

24.FIG. 2h is a cross-sectional view of a semiconductor substrate showing the forming of the step-shaped floating Poly-Si gate of this invention.

25.FIG. 2i is a cross-sectional view of a semiconductor substrate showing the forming of a conformal inter-poly oxide over the step-shaped floating Poly-Si gate of this invention.

26.FIG. 2j is a cross-sectional view of a semiconductor substrate showing the forming of a conformal second polysilicon layer over the inter-poly oxide layer of this invention.

27.FIG. 2k is a cross-sectional view of a semiconductor substrate showing the forming of the step-shaped control Poly-Si gate of this invention.

28.FIG. 2l is a cross-sectional view of a semiconductor substrate showing the ion implanting of the drain and source regions of the step-shaped stacked-gate flash memory cell of this invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

29. Referring now to the drawings, specifically to Figs. FIGS. 2a-2 l, there is shown a preferred method of forming a stacked-gate flash memory cell having a step-shaped floating polysilicon, or, Poly-Si, gate in order to increase the coupling ratio between the floating gate and the control gate of the memory cell. It will become apparent to those skilled in the art that with the disclosure of the one continues rectangular step, other multiply connected surfaces of different shapes can also be formed on the floating gate in order to increase the coupling ratio even more. Such shapes can include triangular, or other nonuniform shapes. It will be evident that the same method disclosed here may be employed in other similar process steps of forming other shapes that are too many to cite here.

30. In FIG. 2a, a substrate (100), preferably silicon, is shown where a layer of gate oxide (110) is formed thereon. The preferred method of forming the gate oxide is by thermal oxidation in dry oxygen carried out in an oxidation furnace in a temperature range between about 850 to 1000° C. Alternatively, other oxidation methods can be used, such as oxidation in dry oxygen and anhydrous hydrogen chloride in an atmospheric or low pressure environment, or low temperature, high-pressure, and the like.

31. Next, a first polysilicon layer (120), later to be formed into a floating gate, is deposited over the gate oxide layer. Polysilicon is formed through methods including but not limited to Low Pressure Chemical Vapor Deposition (LPCVD) methods, Chemical Vapor Deposition (CVD) methods and Physical Vapor Deposition (PVD) sputtering methods employing suitable silicon source materials. Here it is preferred that first polysilicon layer (120) is formed using an LPCVD method employing silane SiH₄ as a silicon source material at a temperature range between about 600 to 700° C. It is also preferred that the thickness of first polysilicon layer (120) is between about 1900 to 2100 Å.

32. Normally, a pad-oxide layer, is next formed over the first polysilicon layer in order to cushion, as is known in the art, the transition of stresses between polysilicon layer (120) and nitride layer (130) to be deposited subsequently. Pad oxide layer may be formed by using chemical CVD SiO₂, but it is preferred that it be grown thermally at a temperature range between about 400 to 700° C., and to a thickness between about 500 to 2500 Å. Since silicon nitride (SiN) has similar properties, sometimes a pad-SiN layer alone is formed by reacting dichlorosilane (SiCl₂H₂) with ammonia (NH₃) in an LPCVD as is shown in FIG. 2b. It is preferred that the thickness of silicon nitride layer (130) is between about 500 to 1500 Å formed at a temperature range between about 600 to 700° C.

33. Then, a first photoresist layer (140) is formed over the nitride layer and patterned to define floating gates to be formed, and the same pattern openings (145) are transferred into the nitride layer as shown in FIG. 2c, by etching. Subsequently, photoresist layer (140) is removed by oxygen plasma ashing and a spacer oxide is formed over the substrate, including the opening (145) as shown in FIG. 2d. It is preferred that the spacer oxide is a TEOS film deposited by the decomposition of tetraethyl orthosilicate at a temperature between about 550 to 700° C. Oxide spacers (155) shown in FIG. 2e are next formed by performing anisotropic etching with gases CF₄ or C₂F₆.

34. As a main feature and key aspect of the present invention, etching is continued further with gases HBr+Cl₂ to form step (125) in first polysilicon layer (120) as shown in FIG. 2f. For a step depth of preferably between about 900 to 1100 Å, the added surface area on the first polysilicon layer is between about 20 to 40% where the higher 40% is preferred. This increase is also reflected in the increased capacitance and therefore in the increased coupling ratio between the floating gate and the control gate to be formed conformally over the floating gate. It will be observed that the surface of the first polysilicon layer exposed in (125) can be “folded” several times over by having several steps or “fins” similar to that is found in heat sinks. Furthermore, the fins can comprise other shapes, such as triangular, or trapezoidal, and so on, all designed to increase the surface area. As another key step, additional area is gained by removing oxide spacers (155) to expose additional polysilicon areas underneath the spacers, as seen in FIG. 2g.

35. The first polysilicon layer exposed in the opening in the nitride layer shown in FIG. 2g is next oxidized to form a thin layer of poly-oxide (160) having a thickness between about 100 to 300 Å. The wet oxidation is performed at a temperature between about 850 to 1000° C. Subsequently, using poly-oxide layer (160) as a hard-mask, nitride layer (130) and first polysilicon layer (110) are removed by etching as shown in FIG. 2h to form a floating Poly-Si gate. This is followed by forming a conformal layer such as tantalum oxide (Ta₂O₅) or oxide-nitride-oxide (ONO) as shown in FIG. 2i. ONO layer (170) is a re-oxidized nitrated oxide, or an oxynitride, where the latter is formed by the nitridization of a thermal oxide layer by thermally annealing the oxide layer with dilute NH₃ using N₂ or Ar as a carrier gas at an elevated temperature usually greater than 800° C. It is preferred that carrier gas N₂ is used at a temperature between about 600 to 700° C. It will be noted that ONO layer (170) so formed is conformal over the step-shaped floating Poly-Si gate as seen in FIG. 2i, and it serves as an inter-poly, or, inter-gate, dielectric layer between the step-shaped floating gate and the control gate to be formed.

36. The control gate of the present invention is also formed conformably by forming a second polysilicon layer over the step-shaped inter-poly ONO layer (170), as shown in FIG. 2j. Preferably, the thickness of second polysilicon layer (180) is between about 1500 to 2000 Å, and is formed by using an LPCVD method employing silane SiH₄ as a silicon source material at a temperature range between about 600 to 700° C. The control gate, as seen in FIG. 2k, is then patterned using a second photoresist layer (not shown). The completion of the stacked-gate flash memory cell of the present invention is accomplished by performing a gate self-aligned source/drain implantation of phosphorous/arsenic ions (190) shown in FIG. 2l at a dosage level between about 5×10¹⁴ to 2×10¹⁵ atoms/cm² and an energy level between about 25 to 45 KeV.

37. Though numerous details of the disclosed method have been set forth here, such as process parameters, to provide an understanding of the present invention, it will be obvious, however, to those skilled in the art that these specific details need not be employed to practice the present invention. At the same time, it will be evident that the same methods may be employed in other similar process steps that are too many to cite, such as the many different multiply connected surfaces of different shapes that can be formed in the manufacture of Poly-Si gates. In other instances, well-known processing steps, such as forming oxide spacers are not described in detail in order not to unnecessarily obscure the present invention.

38. That is to say, while the invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of the invention. 

What is claimed is:
 1. A stacked-gate flash memory cell having a floating Poly-Si gate with multiply connected surfaces of different shapes comprising: providing a semiconductor substrate; a floating Poly-Si gate with multiply connected surfaces of different shapes; an inter-poly dielectric layer over said floating Poly-Si gate; and a Poly-Si control gate over said inter-poly dielectric layer.
 2. A stacked-gate flash memory cell of claim 1 , wherein said floating Poly-Si gate has a thickness between about 1900 to 2100 Å.
 3. A stacked-gate flash memory cell of claim 1 , wherein said multiply connected surfaces have a depth between about 900 to 1100 Å.
 4. A stacked-gate flash memory cell of claim 1 , wherein said different shapes are rectangular and triangular.
 5. A stacked-gate flash memory cell of claim 1 , wherein said inter-poly dielectric layer is oxide-nitride-oxide having a thickness between about 150 to 250 Å.
 6. A stacked-gate flash memory cell of claim 1 , wherein said Poly-Si control gate has a thickness between about 1500 to 2000 Å.
 7. A method of forming a stacked-gate flash memory having a floating Poly-Si gate with multiply connected surfaces of different shapes comprising the steps of: providing a semiconductor substrate; forming a gate-oxide layer over said substrate; forming a first polysilicon layer over said gate-oxide layer; forming multiply connected surfaces of different shapes in said first polysilicon layer; forming a first polysilicon (Poly-Si) floating gate having said surfaces of different shapes; forming an inter-poly oxide layer over said floating Poly-Si gate having said surface of different shapes; and forming a Poly-Si control gate over said floating Poly-Si gate.
 8. The method of claim 7 , wherein said gate-oxide layer has a thickness between about 70 to 150 Å.
 9. The method of claim 7 , wherein said first polysilicon layer has a thickness between about 1900 to 2100 Å.
 10. The method of claim 7 , wherein said multiply connected surfaces have a depth between about 900 to 1100 Å.
 11. The method of claim 7 , wherein said different shapes are rectangular and triangular.
 12. The method of claim 7 , wherein said inter-poly dielectric layer is oxide-nitride-oxide having a thickness between about 150 to 250 Å.
 13. The method of claim 7 , wherein said Poly-Si control gate has a thickness between about 1500 to 2000 Å.
 14. A method of forming a stacked-gate flash memory cell having a step-shaped floating Poly-Si gate comprising the steps of: providing a semiconductor substrate; forming a gate-oxide layer over said substrate; forming a first polysilicon layer over said gate-oxide layer; forming a mask layer over said pad-oxide layer; patterning and forming an opening in said mask layer to define a floating gate region in said substrate; forming spacers in said opening and to expose said first polysilicon layer in said opening; performing a partial etch of said first polysilicon layer exposed in said opening to form a step-shaped surface on said first polysilicon layer; removing said spacers and said mask layer; forming a step-shaped inter-poly dielectric layer over said substrate including said floating Poly-Si gate with said step-shaped surface; forming a second polysilicon layer over said step-shaped inter-poly dielectric layer; removing said second polysilicon layer and underlying said inter-poly oxide layer from said substrate, excluding from regions over floating Poly-Si gate, thus forming a Poly-Si control gate having step-shaped surface corresponding to said floating Poly-Si gate with step-shaped surface; and performing ion implantation to form source and drain of said stacked-gate flash memory cell.
 15. The method of claim 14 , wherein said forming said first polysilicon layer is accomplished using an LPCVD method employing silane SiH₄ as a silicon source material at a temperature range between about 600 to 700° C.
 16. The method of claim 14 , wherein said first polysilicon layer has a thickness between about 1900 to 2100 Å.
 17. The method of claim 14 , wherein said spacer is tetraethyl orthosilicate oxide having a thickness between about 1000 to 2500 Å.
 18. The method of claim 14 , wherein said partial etch of said first polysilicon layer to form said step-shaped surface is accomplished with gases HBr+Cl₂.
 19. The method of claim 14 , wherein said forming said step-shaped inter-poly oxide is accomplished by forming an oxide-nitride-oxide (ONO) layer having a thickness between about 150 to 250 Å.
 20. The method of claim 14 , wherein said second polysilicon layer has a thickness between about 1500 to 2000 Å. 